Indium-doped TiO2 photocatalysts with high-temperature anatase stability
Loading...
Files
Accepted Version
Date
2019-08-05
Authors
Kumaravel, Vignesh
Rhatigan, Stephen
Mathew, Snehamol
Bartlett, John
Nolan, Michael
Hinder, Steven J.
Sharma, Preetam K.
Singh, Anukriti
Byrne, J. Anthony
Harrison, John
Journal Title
Journal ISSN
Volume Title
Publisher
American Chemical Society (ACS)
Published Version
Abstract
The thermal stability of anatase titanium dioxide (TiO2) is a prerequisite to fabricate photocatalyst-coated indoor building materials for use in antimicrobial and self-cleaning applications under normal room light illumination. Metal doping of TiO2 is an appropriate way to control the anatase to rutile phase transition (ART) at high processing temperatures. In this work, ART of indium (In)-doped TiO2 (In–TiO2) was investigated in detail in the range of 500–900 °C. In–TiO2 (In mol % = 0–16) was synthesized via a modified sol–gel approach. These nanoparticles were further characterized by means of powder X-ray diffraction (XRD), Raman, photoluminescence (PL), transient photocurrent response, and X-ray photoelectron spectroscopy (XPS) techniques. XRD results showed that the anatase phase was maintained up to 64% by 16 mol % of In doping at 800 °C of calcination temperature. XPS results revealed that the binding energies of Ti4+ (Ti 2p1/2 and Ti 2p3/2) were red-shifted by In doping. The influence of In doping on the electronic structure and oxygen vacancy formation of anatase TiO2 was studied using density functional theory corrected for on-site Coulomb interactions (DFT+U). First-principles results showed that the charge-compensating oxygen vacancies form spontaneously at sites adjacent to the In dopant. DFT+U calculations revealed the formation of In - 5s states in the band gap of the anatase host. The formation of In2O3 at the anatase surface was also examined using a slab model of the anatase (101) surface modified with a nanocluster of composition In4O6. The formation of a reducing oxygen vacancy also has a moderate energy cost and results in charge localization at In ions of the supported nanocluster. PL and photocurrent measurements suggested that the charge carrier recombination process in TiO2 was reduced in the presence of In dopant. The photocatalytic activity of 2% In–TiO2 calcined at 700 °C is more comparable with that of pure anatase.
Description
Keywords
Impurities , Oxides , Defects in solids , Minerals , Doping
Citation
Kumaravel, V., Rhatigan, S., Mathew, S., Bartlett, J., Nolan, M., Hinder, S. J., Sharma, P. K., Singh, A., Byrne, J. A., Harrison, J. and Pillai, S. C. (2019) 'Indium-doped TiO2 photocatalysts with high-temperature anatase stability', The Journal of Physical Chemistry C, 123 (34), pp.21083-21096. doi: 10.1021/acs.jpcc.9b06811
Link to publisher’s version
Copyright
2019, American Chemical Society. This document is the Accepted Manuscript version of a Published Work that appeared in final form in The Journal of Physical Chemistry C, copyright © American Chemical Society after peer review and technical editing by the publisher. To access the final edited and published work see https://pubs.acs.org/doi/10.1021/acs.jpcc.9b06811